Views: 1 Author: Site Editor Publish Time: 2022-11-08 Origin: Site
How to repair the common damage at the corners of the car tarpaulin? The car tarpaulin is made of high-quality high polymer plastic, with outstanding functions in all aspects. It can provide too fine protection for the surface layout of the car, but it will be damaged after being used for a period of time, especially at corners, such as cracks and broken ropes at corners. If these injuries are not punished in real time, it will not only affect the normal use of the tarpaulin, but also damage the surrounding tarpaulin.
1. The tether at the corner is broken. Sometimes, the lanyard at the corner of the tarpaulin will break, affecting the overall firmness of the tarpaulin. During the repair, the tether with the same material can be used for butt joint to avoid the environment breakage during later use.
2. The tarpaulin in the corner is loosened or even dropped. Whenever some car owners use the tarpaulin, the city will fasten the tether. This time, the tension at the button of the tarpaulin is greater than the force, which will lead to its deformation and scattering of the environment after a long time.
In case of such damage, the tarpaulin eye around the tarpaulin buckle shall not wear the lanyard, otherwise the tarpaulin will crack. During the repair, you can sew a circle of thick stitches around the eyelet. If possible, use nylon wire made of high polymer plastic, and then wear a lanyard.
PVC tarpaulin is a tarpaulin made of high polymer materials, which has outstanding waterproof, flame retardant and aging resistant functions. It is often used to make car tarpaulin, with good application effect.
1. Before making tarpaulin, the tarpaulin manufacturer melts the materials into a coating agent, that is, 100 portions of PVC paste resin, 10 portions of liquid nitrile rubber, 100 portions of filler, 15 portions of flame retardant, 5 portions of stabilizer, 2 portions of mildew inhibitor and 20 portions of pigment are mixed.
2. Other ingredients shall be added by the tarpaulin manufacturer. One to seven parts of cross-linking agent shall be added to the mixed coating agent. After being evenly mixed, it shall be coated on the base cloth and then dried.
3. The tarpaulin manufacturer shall plasticize the coated base cloth, dry the coated base cloth, and then plasticize them to form them.
PVC tarpaulin can be made in large quantities in a short time due to its simple production process, and its functions are very good.